TEIJIN帝人PC Panlite L-1225L物性表物性參數
PC L-1225L是帝人TEIJIN公司聚碳酸酯PC系列型號之一
中國塑商之家旗下全球塑料物性表查詢網,是國內目前最好的PC物性參數PC物性表查詢下載網站,提供TEIJIN帝人Panlite PC中英文雙語版塑料物性數據,塑料物性表,塑膠原料物性大全,專業,嚴謹,規范,完整的物性數據,國際通用的公制和英制單位數據一表同述,簡單明了,通俗易懂,完全吻合國內外人士閱覽習慣.
TEIJIN帝人PC Panlite L-1225L物性表物性參數
以下是TEIJIN帝人PC Panlite L-1225L中英文物性表
|
Teijin Panlite® L-1225L（塑膠原料-聚碳酸酯-PC塑料）
The property table is provided by www.jjy1113.cn, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density 比重
|
1.20 g/cc
|
0.0434 lb/in³
|
ISO 1183
|
|
Water Absorption 吸水率
|
0.20 %
|
0.20 %
|
in water, 23°C, 24h; ISO 62
|
|
Linear Mold Shrinkage 線性收縮率
|
0.0050 - 0.0070 cm/cm
@Thickness 4.00 mm |
0.0050 - 0.0070 in/in
@Thickness 0.157 in |
|
|
Linear Mold Shrinkage, Transverse 線性收縮率/橫向斷裂拉伸強度
|
0.0050 - 0.0070 cm/cm
@Thickness 4.00 mm |
0.0050 - 0.0070 in/in
@Thickness 0.157 in |
|
|
Melt Flow 熔體流動速率
|
21.6 g/10 min
@Load 1.20 kg, Temperature 300 °C |
21.6 g/10 min
@Load 2.65 lb, Temperature 572 °F |
ISO 1133
|
|
Mechanical Properties力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Tensile Strength, Yield 屈服拉伸強度
|
61.0 MPa
|
8850 psi
|
50mm/min; ISO 527
|
|
Elongation at Break 斷裂伸長率
|
>= 50 %
|
>= 50 %
|
50mm/min; ISO 527
|
|
Elongation at Yield 屈服伸長率
|
6.0 %
|
6.0 %
|
50mm/min; ISO 527
|
|
Tensile Modulus 拉伸模量
|
2.40 GPa
|
348 ksi
|
1mm/min; ISO 527
|
|
Flexural Strength 彎曲強度
|
93.0 MPa
|
13500 psi
|
2mm/min; ISO 178
|
|
Flexural Modulus 彎曲彈性模量
|
2.35 GPa
|
341 ksi
|
2mm/min; ISO 178
|
|
Charpy Impact Unnotched 夏比缺口試樣沖擊
|
NB
|
NB
|
ISO 179
|
|
Charpy Impact, Notched 夏比缺口沖擊
|
6.70 J/cm²
|
31.9 ft-lb/in²
|
ISO 179
|
|
Electrical Properties電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Volume Resistivity 體積電阻率
|
>= 1.00e+13 ohm-cm
|
>= 1.00e+13 ohm-cm
|
IEC 60093
|
|
Surface Resistance 表面電阻
|
>= 1.00e+15 ohm
|
>= 1.00e+15 ohm
|
IEC 60093
|
|
Dielectric Constant 介電常數
|
3.0
@Frequency 1e+6 Hz |
3.0
@Frequency 1e+6 Hz |
IEC 60250
|
|
3.1
@Frequency 100 Hz |
3.1
@Frequency 100 Hz |
IEC 60250
|
|
|
Dielectric Strength 介電強度
|
30.0 kV/mm
|
762 kV/in
|
IEC 60243
|
|
Dissipation Factor 耗散因數
|
0.0010
@Frequency 100 Hz |
0.0010
@Frequency 100 Hz |
IEC 60250
|
|
0.0090
@Frequency 1e+6 Hz |
0.0090
@Frequency 1e+6 Hz |
IEC 60250
|
|
|
Comparative Tracking Index 跟蹤指數
|
250 V
|
250 V
|
IEC 60112
|
|
Thermal Properties熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE, linear 線性熱膨脹系數
|
70.0 µm/m-°C
@Temperature 20.0 °C |
38.9 µin/in-°F
@Temperature 68.0 °F |
ISO 11359
|
|
CTE, linear, Transverse to Flow 線性熱膨脹系數/橫向
|
70.0 µm/m-°C
@Temperature 20.0 °C |
38.9 µin/in-°F
@Temperature 68.0 °F |
ISO 11359
|
|
Deflection Temperature at熱變形溫度 0.46 MPa (66 psi)
|
139 °C
|
282 °F
|
ISO 75
|
|
Deflection Temperature at熱變形溫度 1.8 MPa (264 psi)
|
126 °C
|
259 °F
|
ISO 75
|
|
Vicat Softening Point 維卡軟化點
|
146 °C
|
295 °F
|
50°C/hr, 50N; ISO 306
|
|
UL RTI, Electrical 相對溫度指數
|
125 °C
@Thickness 1.47 mm |
257 °F
@Thickness 0.0579 in |
UL 746B
|
|
UL RTI, Mechanical with Impact 機械沖擊熱指數
|
115 °C
@Thickness 1.47 mm |
239 °F
@Thickness 0.0579 in |
UL 746B
|
|
UL RTI, Mechanical without Impact無機械沖擊熱指數
|
125 °C
@Thickness 1.47 mm |
257 °F
@Thickness 0.0579 in |
UL 746B
|
|
Flammability, UL94 阻燃等級
|
HB
@Thickness 1.90 mm |
HB
@Thickness 0.0748 in |
|
|
V-2
@Thickness 0.400 mm |
V-2
@Thickness 0.0157 in |
||
|
Optical Properties光學性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Refractive Index 折射率
|
1.585
|
1.585
|
ASTM D542
|
|
Transmission, Visible 透光率
|
88 %
@Thickness 3.00 mm |
88 %
@Thickness 0.118 in |
ASTM D1003
|