PC L-1250Y是帝人TEIJIN公司聚碳酸酯PC系列型號之一
中國塑商之家旗下全球塑料物性表查詢網,是國內目前最好的PC物性參數PC物性表查詢下載網站,提供TEIJIN帝人Panlite PC中英文雙語版塑料物性數據,塑料物性表,塑膠原料物性大全,專業,嚴謹,規范,完整的物性數據,國際通用的公制和英制單位數據一表同述,簡單明了,通俗易懂,完全吻合國內外人士閱覽習慣.
TEIJIN帝人PC Panlite L-1250Y物性表物性參數
以下是TEIJIN帝人PC Panlite L-1250Y中英文物性表
|
Teijin Panlite® L-1250Y（塑料-聚碳酸酯-PC）
The property table is provided by www.jjy1113.cn, welcome to download, reprint please indicate the source!
|
|||
|
Physical Properties
物理性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Density 比重
|
1.20 g/cc
|
0.0434 lb/in³
|
ASTM D792
|
|
Water Absorption 吸水率
|
0.20 %
|
0.20 %
|
23°C; 24 hr; ASTM D570
|
|
Linear Mold Shrinkage，Flow 線性收縮率/流動
|
0.0050 - 0.0070 cm/cm
|
0.0050 - 0.0070 in/in
|
ASTM D955
|
|
Linear Mold Shrinkage，Transverse 線性收縮率/橫向
|
0.0050 - 0.0070 cm/cm
|
0.0050 - 0.0070 in/in
|
ASTM D955
|
|
Mechanical Properties
力學性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Hardness，Rockwell
羅氏硬度M
|
77
|
ASTM D785
|
|
|
Tensile Strength，Ultimate 極限拉伸強度
|
81.0 MPa
|
11700 psi
|
ASTM D638
|
|
Tensile Strength，Yield
屈服拉伸強度
|
61.0 MPa
|
8850 psi
|
ASTM D638
|
|
Elongation at Break
斷裂伸長率
|
140 %
|
140 %
|
ASTM D638
|
|
Elongation at Yield
屈服伸長率
|
6.0 %
|
6.0 %
|
ASTM D638
|
|
Tensile Modulus
拉伸模量
|
2.12 GPa
|
307 ksi
|
ASTM D638
|
|
Flexural Yield Strength
彎曲屈服強度
|
90.0 MPa
|
13100 psi
|
ASTM D790
|
|
Flexural Modulus
彎曲彈性模量
|
2.23 GPa
|
323 ksi
|
ASTM D790
|
|
Compressive Yield Strength壓縮屈服強度
|
76.0 MPa
|
11000 psi
|
ASTM D695
|
|
Izod Impact，Notched
懸臂梁缺口沖擊強度
|
1.40 J/cm
@Thickness 6.40 mm |
2.62 ft-lb/in
@Thickness 0.252 in |
ASTM D256
|
|
8.80 J/cm
@Thickness 3.20 mm |
16.5 ft-lb/in
@Thickness 0.126 in |
ASTM D256
|
|
|
Electrical Properties
電性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Electrical Resistivity
電阻率
|
3.00e+16 ohm-cm
|
3.00e+16 ohm-cm
|
ASTM D257
|
|
Dielectric Constant
介電常數
|
2.9
@Frequency 60 Hz |
2.9
@Frequency 60 Hz |
ASTM D150
|
|
2.95
@Frequency 1e+6 Hz |
2.95
@Frequency 1e+6 Hz |
ASTM D150
|
|
|
Dielectric Strength
介電強度
|
30.0 kV/mm
@Thickness 1.60 mm |
762 kV/in
@Thickness 0.0630 in |
quick pressure rise method; ASTM D149
|
|
Dissipation Factor
耗散因數
|
0.00040
@Frequency 60 Hz |
0.00040
@Frequency 60 Hz |
ASTM D150
|
|
0.0090
@Frequency 1e+6 Hz |
0.0090
@Frequency 1e+6 Hz |
ASTM D150
|
|
|
Arc Resistance 耐電弧性
|
110 sec
|
110 sec
|
ASTM D495
|
|
Comparative Tracking Index 跟蹤指數
|
300 V
|
300 V
|
IEC 112
|
|
Thermal Properties
熱性能
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
CTE，linear
線性熱膨脹系數
|
70.0 µm/m-°C
@Temperature 20.0 °C |
38.9 µin/in-°F
@Temperature 68.0 °F |
Flow Direction; ASTM D696
|
|
CTE，linear，Transverse to Flow 線性熱膨脹系數/橫向
|
70.0 µm/m-°C
@Temperature 20.0 °C |
38.9 µin/in-°F
@Temperature 68.0 °F |
ASTM D696
|
|
Deflection Temperature at熱變形溫度 0.46 MPa (66 psi)
|
143 °C
|
289 °F
|
ASTM D648
|
|
Deflection Temperature at熱變形溫度 1.8 MPa (264 psi)
|
133 °C
|
271 °F
|
ASTM D648
|
|
UL RTI，Electrical
相對溫度指數
|
125 °C
@Thickness 1.47 mm |
257 °F
@Thickness 0.0579 in |
|
|
UL RTI，Mechanical with Impact 機械沖擊熱指數
|
115 °C
@Thickness 1.47 mm |
239 °F
@Thickness 0.0579 in |
|
|
UL RTI，Mechanical without Impact無機械沖擊熱指數
|
125 °C
@Thickness 1.47 mm |
257 °F
@Thickness 0.0579 in |
|
|
Flammability，UL94
阻燃等級
|
V-2
@Thickness 1.47 mm |
V-2
@Thickness 0.0579 in |
|
|
V-2
@Thickness 3.05 mm |
V-2
@Thickness 0.120 in |
||
|
Optical Properties
光學性質
|
Metric公制數據
|
English英制數據
|
Comments測試方法
|
|
Refractive Index折射率
|
1.585
|
1.585
|
ASTM D542
|
|
Transmission，Visible
透光率
|
89 %
@Thickness 3.00 mm |
89 %
@Thickness 0.118 in |
|